Complex Concaved Cuboctahedrons of Copper Sulfide Crystals with Highly Geometrical Symmetry Created by a Solution Process

Supporting Info

Chunyan Wu,^† Shu-Hong Yu,*^† and Markus Antonietti^§

Division of Nanomaterials and Chemistry, Hefei National Laboratory for Physical Sciences at Microscale, Department of Chemistry, University of Science and Technology of China, Hefei, Anhui 230026, People's Republic of China, and Department of Colloid Chemistry, Max Planck Institute of Colloids and Interfaces, MPI Research Campus Golm, D-14424 Potsdam, Germany

Chem. Mater., 2006, 18 (16), pp 3599–3601

DOI: 10.1021/cm060956u

Publication Date (Web): July 15, 2006

†

Hefei National Laboratory for Physical Sciences at Microscale.

Corresponding author. E-mail: shyu@ustc.edu.cn. Fax: 86 551 3603040.

Max Planck Institute of Colloids and Interfaces.

View: Full Text HTML | Hi-Res PDF

Tools

SciFinder Links

History

Published In Issue August 08, 2006
Received April 25, 2006
Revised Manuscript Received June 18, 2006

Recommend & Share

Related Content

Acetic Acid-Assisted Solution Process for Growth of Complex Copper Sulfide Microtubes Constructed by Hexagonal NanoflakesChemistry of Materials
- Acetic Acid-Assisted Solution Process for Growth of Complex Copper Sulfide Microtubes Constructed by Hexagonal Nanoflakes
  Jun-Yan Gong, Shu-Hong Yu, Hai-Sheng Qian, Lin-Bao Luo, and Xian-Ming Liu
  Chemistry of Materials 2006 18 (8), pp 2012–2015
  Abstract: An acetic acid-assisted solution reaction at 80 °C has been developed to synthesize complex CuS microtubes with a diameter about 800 nm and length up to 16 μm, which were constructed by hexagonal copper sulfide nanoflakes. The formation process of complex ...
  Abstract | Full Text HTML | Hi-Res PDF
Surfactant-Assisted Hydrothermal Synthesis and Magnetic Properties of Urchin-like MnWO₄ MicrospheresThe Journal of Physical Chemistry C
- Surfactant-Assisted Hydrothermal Synthesis and Magnetic Properties of Urchin-like MnWO₄ Microspheres
  Yu-Xue Zhou, Qiao Zhang, Jun-Yan Gong and Shu-Hong Yu
  The Journal of Physical Chemistry C 2008 112 (35), pp 13383–13389
  Abstract: Three-dimensional (3D) urchin-like MnWO₄ microspheres with a diameter of ca. 1−1.2 μm assembled by nanorods with a length of 240 nm and an aspect ratio of ca. 9 have been fabricated by a cationic surfactant cetyltrimethyl ammonium bromide (CTAB) assisted ...
  Abstract | Full Text HTML | PDF w/ Links | Hi-Res PDF
Loading of Silica Spheres on Concaved CuS Cuboctahedrons Using 3-Aminopropyltrimethoxysilane as a LinkerLangmuir
- Loading of Silica Spheres on Concaved CuS Cuboctahedrons Using 3-Aminopropyltrimethoxysilane as a Linker
  Yong Wan, Chunyan Wu, Yulin Min, and Shu-Hong Yu
  Langmuir 2007 23 (16), pp 8526–8530
  Abstract: A new composite structure made of unique CuS cuboctahedron crystals and coating silica spheres with diameters ranged from 30 to 730 nm has been demonstrated. 3-Aminopropyltrimethoxysilane acted as a linker, which provided hydrogen bonding and metal−ligand ...
  Abstract | Full Text HTML | Hi-Res PDF